Users in the dust wire-drawing machine equipment, it is inevitable to encounter problems such as broken wire. There are many reasons for this problem. In order to help you better solve this problem, today we will analyze the reasons for you, and will give some Suggestions. Let's take a look at the details.
The first reason is that the joint is not strong. If this is the case, then we should timely adjust the parameter Settings of the welding machine's current, top pressure and power on time, so as to improve the welding quality. The second reason is due to the use of wire contains some inclusions, resulting in the wire drawing machine equipment by the situation of fracture. If this is the case, then we should strengthen the acceptance management of the production blank.
The third reason is the selection of the mold does not meet the requirements. For this problem, we should timely re-selection, combined with the actual process requirements, appropriate adjustment of the requirements of the mold, so as to eliminate the deformation is too large or too small phenomenon; The fourth reason is that the counterforce is too large. Under normal circumstances, wire drawing machine equipment tension should be controlled in a certain range, and the number of tower wheel winding to be reasonable.
The fifth reason is due to the choice of mold hole shape is not reasonable, or smoothness does not meet the requirements. Therefore, we must strictly comply with the standard repair line mold, workspace deformation Angle should ensure that the use of requirements, wire drawing machine line mold diameter area can not be too long, after polishing the mold hole finish to meet the requirements. The sixth reason is that pickling is not thorough. At this time, we should readjust the acid temperature, concentration, strengthen washing and neutralization.
In addition, there is a very important reason, may also lead to wire drawing machine broken problem, that is, the quality of the wire billet used is not good. In this case, we should st